5086 aluminium alloy

5086 aluminium alloy is an aluminium–magnesium alloy, primarily alloyed with magnesium. It is not strengthened by heat treatment, instead becoming stronger due to strain hardening, or cold mechanical working of the material.

Since heat treatment doesn't strongly affect the strength, 5086 can be readily welded and retain most of its mechanical strength. The good results with welding and good corrosion properties in seawater make 5086 extremely popular for vessel gangways, building boat and yacht hulls.[1]

Basic properties

5086 has a density of 2.660 kg/dm3 (0.0961 lb/cu in), with a specific gravity of 2.66.

Melting point is 590 °C (1,090 °F).

Chemical properties

The alloy composition of 5086 is:[2]

Mechanical properties

The mechanical properties of 5086 vary significantly with hardening and temperature.[2]

–O hardening

Unhardened 5086 has a yield strength of 120 MPa (17 ksi) and ultimate tensile strength of 260 MPa (38 ksi) from −28 to 100 °C (−18 to 212 °F). At cryogenic temperatures it is slightly stronger: at −196 °C (−321 °F), yield of 130 MPa (19 ksi) and ultimate tensile strength of 380 MPa (55 ksi); above 100 °C (212 °F) its strength is reduced.

Elongation, the strain before material failure, ranges from 46% at −196 °C (−321 °F), 35% at −80 °C (−112 °F), 32% at −28 °C (−18 °F), 22% at 20 °C (68 °F), 30% at 24 °C (75 °F), 36% at 100 °C (212 °F), and increases above there.

–H32 hardening

–H116 hardening

H116 strain hardened 5086, with properties measured at 20 °C (68 °F), has yield strength of 210 MPa (30 ksi), ultimate tensile strength of 290 MPa (42 ksi), and elongation of 12%.

Uses

5086 is the preferred hull material for small aluminium boats or larger yachts. Its high strength and good corrosion resistance make it an excellent match for yachting.[1]

5086 has a tendency to undergo Stress corrosion cracking and is not used much in aircraft construction as a result.[3]

5086 has been used in vehicle armor, notably in the M113 Armored Personnel Carrier and M2 Bradley Infantry fighting vehicle.

Welding

5086 is often assembled using arc welding, typically MIG or TIG welding. The newer technique of Friction stir welding has also been successfully applied but is not in common use.

Arc welding reduces mechanical properties to no worse than –O hardening condition. For –H116 base material, measured at 20 °C (68 °F) ambient temperature, yield strength decreases from 210 MPa (30 ksi) to 120 MPa (17 ksi) and ultimate strength from 290 to 260 MPa (42 to 38 ksi). The relatively low decrease in ultimate strength (about 10%) is extremely good performance for an aluminium alloy.

References
  1. Boatbuilding with Aluminum, Stephen F. Pollard, 1993, ISBN 978-0-07-050426-4
  2. 5086 Material properties at supplliersonline.com, accessed October 29, 2006
  3. 5xxx Plate information sheet Archived 2006-10-26 at the Wayback Machine at www.alcoa.com, accessed October 29, 2006

Further reading
  • "Properties of Wrought Aluminum and Aluminum Alloys: 5086, Alclad 5086", Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, Vol 2, ASM Handbook, ASM International, 1990, p. 93-4.