Conformal coating

Conformal coatings are used to protect electronic components from the environmental factors they are exposed to. Examples of these factors include moisture, dust, salt, chemicals, temperature changes and mechanical abrasion, as well as corrosion. More recently, conformal coatings are being used to reduce the formation of whiskers,[2] and can also prevent current bleed between closely positioned components.

Conformal coatings are breathable, allowing trapped moisture in electronic boards to escape while maintaining protection from contamination. These coatings are not sealants, and prolonged exposure to vapors will cause transmission and degradation to occur. There are typically four classes of conformal coatings: Acrylic, Urethane, Silicone, and Varnish. While each has its own specific physical and chemical properties each is able to perform the following functions:

• Insulation: Allowing closer conductor spacing
• Minimal effect on component weight
• More board protection including that of environmental, chemical, and corrosive

Conformal coatings of PCBA where it is UV-cured

Precision analog circuitry may suffer degraded accuracy if insulating surfaces become contaminated with ionic substances such as fingerprint residues, which can become mildly conductive in the presence of moisture or heightened humidity. A suitably chosen material coating can reduce the effects of mechanical stress and vibrations on the circuit and its ability to perform in extreme temperatures.

For example, in a chip-on-board assembly process, a silicon die is mounted on the board with an adhesive or soldering process, then electrically connected by wire bonding, typically with 0.001-inch-diameter gold or aluminum wire. The chip and the wire are delicate, so they are encapsulated in a version of conformal coating called a blob top. This p

prevents accidental contact from damaging the wires or the chip. Another use of conformal coating[3] is to increase the voltage rating of a dense circuit assembly. An insulating coating can withstand a much stronger electric field than air, particularly at high altitudes.

Except for Parylene, most organic coatings are easily penetrated by water molecules. A coating preserves the performance of electronics primarily by preventing ionizable contaminants such as salts from reaching circuit nodes and combining with water to form a microscopically thin electrolyte film. For this reason, the coating is far more effective if all surface contamination is removed first, using a highly repeatable industrial process such as vapor degreasing or semi-aqueous washing. Extreme cleanliness also improves adhesion. Pinholes defeat the purpose of the coating because a contaminant film would make contact with circuit nodes and form undesired conductive paths.

The coating material can be applied by various methods. This includes brushing, spraying, dipping or selectively coating by robots. Different methods of curing and drying are available depending on the conformal coating material. Nearly all modern conformal coatings contain a fluorescent dye to aid in coating coverage inspection.[4]

Spray application coating

See also: chemical vapor deposition and atomic layer deposition

Conformal Coating Spray booth

This coating can be completed with a spray aerosol or spray booth with a spray gun and is suitable for low and medium-volume processing.[7] The quality of the surface finish can be superior to all other methods when a skilled operator completes the process, provided that the circuit board is clean and the coating has no adhesion problems. The coating application may be limited due to 3D effects. Masking requirements are more of a shield nature rather than a barrier since there is less penetration. The lack of penetration can be a problem where the coating is desired to penetrate beneath devices.

Spray application can be one of the most cost-effective ways of applying conformal coating, as it can be done on the bench top for small rework and repair jobs. This method can be done in spray booths for medium-scale production.[6]

One of the key attributes of atomized spraying is giving excellent tip coverage to components. When conformal coatings are applied to a PCB, they have a tendency to slump. The first layer of a coating can give a thin edge on the corners of components. This can be improved with a second coat by double-dipping or brushing, but this is a repeat process and may not be acceptable. To eliminate this problem, atomized spraying can be used.

Conformal coating dipping

Conformal Coating Dip System

This coating is a highly repeatable process. If the printed circuit board (PCB) is designed correctly, it can be the highest volume technique.[7] The coating penetrates everywhere, including beneath devices, hence, masking must be perfect to prevent leakage. Therefore, many PCBs are unsuitable for dipping due to their design.

The issue of thin tip coverage where the material slumps around sharp edges ,can be a problem, especially in a condensing atmosphere. This tip coverage effect can be eliminated by either double dipping the PCB or using several thin layers of atomized spraying to achieve good coverage without exceeding coating thickness recommendations. A combination of the two techniques may also be used.

Coating material (after curing) should have a thickness of 30–130 μm (0.0012–0.0051 in) when using acrylic resin, epoxy resin, or urethane resin. For silicone resin, the coating thickness recommended by the IPC standards is 50–210 μm (0.0020–0.0083 in).

There are several methods for measuring coating thickness, and they fall into two categories: wet film and dry film.

Wet film conformal coating measurement

Wet film gauge for Conformal Coating Thickness Measurement

The wet film method ensures quality control while the coating is still wet.

Applying too much coating can be expensive. Also, wet film measurements are useful for conformal coatings where the dry film thickness can only be measured destructively or where over-application of conformal coating is a problem.

The wet film gauges are applied to the wet conformal coating; the teeth indicate the coating thickness. The dry film thickness can then be calculated from the measurement.

Dry film conformal coating thickness measurement

Dry film Conformal Coating Thickness Measurement

An alternative to wet film measurement is by using eddy currents. The system works by placing the test head on the surface of the conformal coating. The measurement is almost instantaneous and provides an immediate repeatable result for thickness measurement.

Test coupons are the ideal method for measuring coating thickness, and can be archived as a physical record. Apply the coating to test coupons at the same time as the circuit boards providing a permanent record of coating thickness.

Thicker coatings or better-applied coatings may be required when liquid water is present due to possible pinhole formation in the coating[5] or when the coating is too thin on the sharp edges of components due to poor application. This is considered a defect and can be eliminated with appropriate steps and training. These techniques effectively "pot" or "conform" to components by completely covering them.

Conformal Coating Inspection Booth

Conformal Coating AOI

Traditionally, conformal coating inspection has been done manually. A typical situation is an inspector sitting in a booth, examining each PCB under a high intensity long wave UV lamp. The inspector checks for proper workmanship and that standards are met.

Recent developments in conformal coating automated optical inspection (AOI) have begun to address these manual processes and issues. Automated Inspection Systems can be camera- or scanner-based, hence the technology can be matched to the project.

The selection of conformal coating material needs to be done carefully, and in relation to the application method.[16][17] Incorrect selection can affect long term reliability of the circuit board, and can cause processing and cost problems.

The most common standards for conformal coating are IPC A-610[18] and IPC-CC-830.[19] These standards list indications of good and bad coverage and describe various failure mechanisms such as dewetting[20] and orange peel.[21]

Another type of coating called parylene is applied with a vacuum deposition process at ambient temperature. Film coatings from 0.100 to 76 μm can be applied in a single operation. The advantage of parylene coatings is that they cover hidden surfaces and other areas where spray and needle application are not possible. Coating thickness is uniform, even on irregular surfaces. Desired contact points such as battery contacts or connectors must be covered with an air-tight mask to prevent the parylene from coating the contacts. Applying parylene is a batch process which does not lend itself to high volume processing. The cost per PCB can be high due to high capital investment and the cost per batch.

There are many chemistry of conformal coatings available. It is important to choose a coating chemistry meeting the application needs. Below are five common attributes for each coating chemistry:[22][23]

Acrylic

• Ease of rework
• Simple drying process
• Good moisture resistance
• High fluorescence level
• Ease of viscosity adjustment

Epoxy

• Useful to about 150C [302F]
• Harder durometer, abrasion resistance
• CTE closer to epoxy PCB substrate
• Higher Tg (Glass transition)
• Good dielectric properties

Polyurethane

• Good dielectric properties
• Good moisture resistance
• Solvent resistance
• Less reversion potential
• Abrasion resistance

Silicone

• Stable over wide temperature range (in general, -40C to 200C)[-40F to 392F]
• Flexible, provides dampening and impact protection
• Good moisture resistance
• High dielectric strength
• Low surface energy for better wetting

Fluorinated or non Fluorinated - Poly-Para-Xylylene (Parylene)

• Excellent uniformity regardless of part geometry
• Chemical inertness
• Minimal added mass and low out-gassing
• Low environmental impact process
• Low dielectric constant

Amorphous Fluoropolymer

• Low dielectric constant
• High glass transition temperature
• Low surface energy
• Low water absorption
• Solvent resistance

The basics of conformal coating processing are found in a presentation available at:[24]

Selecting the correct coating material is one of the process engineer's most critical decisions. This criteria includes:[25]

• What is being protected against? (e.g., moisture, chemicals)
• What temperature range will the electrical device encounter?
• What are the physical, electrical, and chemical requirements for the coating material itself?
• Electrical, chemical, and mechanical compatibility with the parts and substances to be coated (for instance, does it need to match the coefficient of expansion of chip components?)

Answers will determine the suitability of a particular material, be it acrylic, polyurethane, silicone, epoxy, etc. Process, production and commercial issues will then enter the equation:

• How easily can the material be reworked once applied?
• How fast does the material dry (cure)?[26]
• How fast can the material be applied and dried (throughout time)?[26]
• What type of process and equipment is necessary to achieve the required coating quality (uniformity and repeatability)?[27]
• Price of the material.
• Quality of the material supplied (two acrylic material manufacturers will not produce equal quality of material).