Organic superconductor

Fabre-salts are composed of tetramethyltetrathiafulvalene (TMTTF) and Bechgaard salts of tetramethyltetraselenafulvalene (TMTSF). These two organic molecules are similar except for the sulfur-atoms of TMTTF being replaced by selenium-atoms in TMTSF. The molecules are stacked in columns (with a tendency to dimerization) which are separated by anions. Typical anions are, for example, octahedral PF₆, AsF₆ or tetrahedral ClO₄ or ReO₄.

Both material classes are quasi-one-dimensional at room-temperature, only conducting along the molecule stacks, and share a very rich phase diagram containing antiferromagnetic ordering, charge order, spin-density wave state, dimensional crossover and superconductivity.

Only one Bechgaard salt was found to be superconducting at ambient pressure which is (TMTTF)₂ClO₄ with a transition temperature of T_C = 1.4 K. Several other salts become superconducting only under external pressure. The external pressure required to drive most Fabre-salts to superconductivity is so high, that under lab conditions superconductivity was observed only in one compound. A selection of the transition temperature and corresponding external pressure of several one-dimensional organic superconductors is shown in the table below.

The layered structure of ET₂X salts illustrated by κ-(ET)₂Cu₂(CN)₃. The yellow, grey, blue and red ellipsoids represent the sulfur, carbon, nitrogen and copper atoms, respectively. The hydrogen atoms are omitted for clarity. Layers of ET donor molecules are separated by polymeric Cu₂(CN)₃^- anion sheets. κ-(ET)₂Cu₂(CN)₃ is a semiconductor, but a very similar κ'-(ET)₂Cu₂(CN)₃ polymorph is an ambient-pressure superconductor with T_C ~ 5 K.[4]

BEDT-TTF is the short form of bisethylenedithio-tetrathiafulvalene commonly abbreviated with ET. These molecules form planes which are separated by anions. The pattern of the molecules in the planes is not unique but there are several different phases growing, depending on the anion and the growth conditions. Important phases concerning superconductivity are the α- and θ- phase with the molecules ordering in a fishbone structure and the β- and especially κ-phase which order in a checkerboard structure with molecules being dimerized in the κ-phase. This dimerization makes the κ-phases special as they are not quarter- but half-filled systems, driving them into superconductivity at higher temperatures compared to the other phases.

The amount of possible anions separating two sheets of ET-molecules is nearly infinite. There are simple anions such as triiodide (I⁻
₃), polymeric ones such as the very famous Cu[N(CN)₂]Br and anions containing solvents for example Ag(CF₃)₄·112DCBE. The electronic properties of the ET-based crystals are determined by its growing phase, its anion and by the external pressure applied. The external pressure needed to drive an ET-salt with insulating ground state to a superconducting one is much less than those needed for Bechgaard salts. For example, κ-(ET)₂Cu[N(CN)₂]Cl needs only a pressure of about 300 bar to become superconducting, which can be achieved by placing a crystal in grease frozen below 0 °C (32 °F) and then providing sufficient stress to induce the superconducting transition. The crystals are very sensitive, which can be observed impressively in α-(ET)₂I₃ lying several hours in the sun (or more controlled in an oven at 40 °C, 104 °F). After this treatment one gets α_Tempered-(ET)₂I₃ which is superconducting.

In contrast to the Fabre or Bechgaard salts universal phase diagrams for all the ET-based salts have only been proposed yet. Such a phase diagram would depend not only on temperature and pressure (i.e. bandwidth), but also on electronic correlations. In addition to the superconducting ground state these materials show charge-order, antiferromagnetism or remain metallic down to lowest temperatures. One compound is even predicted to be a spin liquid.

The highest transition temperatures at ambient pressure and with external pressure are both found in κ-phases with very similar anions. κ-(ET)₂Cu[N(CN)₂]Br becomes superconducting at T_C = 11.8 K at ambient pressure, and a pressure of 300 bar drives deuterated κ-(ET)₂Cu[N(CN)₂]Cl from an antiferromagnetic to a superconducting ground state with a transition temperature of T_C = 13.1 K. The following table shows only a few exemplary superconductors of this class. For more superconductors, see Lebed (2008) in the references.

Even more superconductors can be found by changing the ET-molecules slightly either by replacing the sulfur atoms by selenium (BEDT-TSF, BETS) or by oxygen (BEDO-TTF, BEDO).

Some two-dimensional organic superconductors of the κ-(ET)₂X and λ(BETS)₂X families are candidates for the Fulde-Ferrell-Larkin-Ovchinnikov (FFLO) phase when superconductivity is suppressed by an external magnetic field.[5]

Structure of Cs₃C₆₀

Superconducting fullerenes based on C₆₀ are fairly different from other organic superconductors. The building molecules are no longer manipulated hydrocarbons but pure carbon molecules. In addition these molecules are no longer flat but bulky which gives rise to a three-dimensional, isotropic superconductor. The pure C₆₀ grows in an fcc-lattice and is an insulator. By placing alkali atoms in the interstitials the crystal becomes metallic and eventually superconducting at low temperatures.

Unfortunately C₆₀ crystals are not stable at ambient atmosphere. They are grown and investigated in closed capsules, limiting the measurement techniques possible. The highest transition temperature measured so far was T_C = 33 K for Cs₂RbC₆₀.The highest measured transition temperature of an organic superconductor was found in 1995 in Cs₃C₆₀ pressurized with 15 kbar to be T_C = 40 K. Under pressure this compound shows a unique behavior. Usually the highest T_C is achieved with the lowest pressure necessary to drive the transition. Further increase of the pressure usually reduces the transition temperature. However, in Cs₃C₆₀ superconductivity sets in at very low pressures of several 100 bar, and the transition temperature keeps increasing with increasing pressure. This indicates a completely different mechanism then just broadening of the bandwidth.

Next to the three major classes of organic superconductors (SCs) there are more organic systems becoming superconducting at low temperatures or under pressure. A few examples follow.

Graphite intercalation SCs

Crystal structure of KC₈

Putting foreign molecules or atoms between hexagon graphite sheets leads to ordered structures and to superconductivity even if neither the foreign molecule or atom nor the graphite layers are metallic. Several stoichiometries have been synthesized using mainly alkali atoms as anions.