Pickling (metal)

Pickling is a metal surface treatment used to remove impurities, such as stains, inorganic contaminants, and rust or scale from ferrous metals, copper, precious metals and aluminum alloys.[1] A solution called pickle liquor, which usually contains acid, is used to remove the surface impurities. It is commonly used to descale or clean steel in various steelmaking processes.

Process
Further information: Hydrochloric acid § Pickling of steel

Metal surfaces can contain impurities that may affect usage of the product or further processing like plating with metal or painting. Various chemical solutions are usually used to clean these impurities. Strong acids, such as hydrochloric acid and sulfuric acid are common, but different applications use various other acids. Also alkaline solutions can be used for cleaning metal surfaces. Solutions usually also contain additives such as wetting agents and corrosion inhibitors. Pickling is sometimes called acid cleaning if descaling is not needed.[2][3]

Many hot working processes and other processes that occur at high temperatures leave a discoloring oxide layer or scale on the surface. In order to remove the scale the workpiece is dipped into a vat of pickle liquor. Prior to cold rolling operation, hot rolled steel is normally passed through a pickling line so as to eradicate the scale from the surface.

The primary acid used in steelmaking is hydrochloric acid, although sulfuric acid was previously more common. Hydrochloric acid is more expensive than sulfuric acid, but it pickles much faster while minimizing base metal loss. The speed is a requirement for integration in automatic steel mills that run production at speeds as high as 800 ft/min (≈243 metres/min).[4]

Carbon steels, with an alloy content less than or equal to 6%, are often pickled in hydrochloric or sulfuric acid. Steels with an alloy content greater than 6% must be pickled in two steps and other acids are used, such as phosphoric, nitric and hydrofluoric acid. Rust- and acid-resistant chromium-nickel steels are pickled traditionally in a bath of hydrofluoric and nitric acid.[5] Most copper alloys are pickled in dilute sulfuric acid, but brass is pickled in concentrated sulfuric and nitric acid mixed with sodium chloride and soot.[1]

In jewelry making, pickling is used to remove the copper oxide layer that results from heating copper and sterling silver during soldering and annealing. A diluted sulfuric acid pickling bath is traditionally used,[6] but may be replaced with citric acid.

Sheet steel that undergoes acid pickling will oxidize (rust) when exposed to atmospheric conditions of moderately high humidity. For this reason, a thin film of oil or similar waterproof coating is applied to create a barrier to moisture in the air. This oil film must later be removed for many fabrication, plating or painting processes.

Disadvantages

Acid cleaning has limitations in that it is difficult to handle because of its corrosiveness, and it is not applicable to all steels. Hydrogen embrittlement becomes a problem for some alloys and high-carbon steels. The hydrogen from the acid reacts with the surface and makes it brittle, causing cracks. Because of its high reactivity with treatable steels, acid concentrations and solution temperatures must be kept under control to ensure desired pickling rates.

Waste products

Pickling sludge is the waste product from pickling, and includes acidic rinse waters, iron chlorides, and metallic salts and waste acid.[7] Spent pickle liquor is considered a hazardous waste by the EPA.[8] Pickle sludge from steel processes is usually neutralized with lime and disposed of in a landfill since the EPA no longer deems it a hazardous waste after neutralization.[8] The lime neutralization process raises the pH of the spent acid. The waste material is subject to a waste determination to ensure no characteristic or listed waste is present.[9] Since the 1960s, hydrochloric pickling sludge is often treated in a hydrochloric acid regeneration system, which recovers some of the hydrochloric acid and ferric oxide. The rest must still be neutralized and disposed of in land fills[10] or managed as a hazardous waste based on the waste profile analysis.[9] The by-products of nitric acid pickling are marketable to other industries, such as fertilizer processors.[11]

Alternatives

Smooth clean surface (SCS) and eco pickled surface (EPS) are more recent alternatives. In the SCS process, surface oxidation is removed using an engineered abrasive and the process leaves the surface resistant to subsequent oxidation without the need for oil film or other protective coating. EPS is a more direct replacement for acid pickling. Acid pickling relies on chemical reactions while EPS uses mechanical means. The EPS process is considered "environmentally friendly" compared with acid pickling and it imparts to carbon steel a high degree of rust resistance, eliminating the need to apply the oil coating that serves as a barrier to oxidation for acid-pickled carbon steel.

Alternative methods include also mechanical cleaning such as abrasive blasting, grinding, wire brushing, hydrocleaning and Laser cleaning. These methods generally do not provide as clean a surface as pickling does[12][13]

References
  1. Eagleson, Mary (1994). Concise Encyclopedia Chemistry (revised ed.). Berlin: Walter de Gruyter. p. 834. ISBN 978-3-11-011451-5.
  2. ASM handbook. ASM International. Handbook Committee. (10th ed.). Materials Park, Ohio. ISBN 9780871703842. OCLC 21034891.{{cite book}}: CS1 maint: others (link)
  3. American Electroplaters and Surface Finishers Society (2002). Proceedings AESF SUR/FIN 2002: Annual International Technical Conference June 24-27, 2002, Chicago, IL. Orlando, FL: American Electroplaters and Surface Finishers Society. OCLC 224057432.
  4. Liu, David; Lipták, Béla G. (1997). Environmental engineers' handbook. CRC Press. p. 973. ISBN 978-0-8493-9971-8.
  5. "Pickling and Passivation". Australian Stainless Steel Development Association. Brisbane, Australia. Archived from the original on 2021-05-20.
  6. Fisch, Arline M. (2003). Textile Techniques in Metal: For Jewelers, Textile Artists & Sculptors. Lark Books. p. 32. ISBN 978-1-57990-514-9.
  7. Rao, S. Ramachandra (2006). Resource recovery and recycling from metallurgical wastes. Elsevier. pp. 179–180. ISBN 978-0-08-045131-2.
  8. McCoy's RCRA Unraveled. Paul V. Gallagher, Eric J. Weber, Paula J. Menten, McCoy & Associates. Lakewood, CO: McCoy and Associates. 2007. ISBN 978-0-930469-43-6. OCLC 845356452.{{cite book}}: CS1 maint: date and year (link) CS1 maint: others (link)
  9. "Electronic Code of Federal Regulations". U.S. Government Printing Office. Archived from the original on 2014-06-14. Retrieved 2013-03-21.
  10. International Iron and Steel Institute (1997). Steel Industry and the Environment: Technical and Management Issues. Vol. 38. Tim Jones. United Nations Environment Program. Industry and Environment. p. 76. ISBN 978-92-807-1651-1.
  11. Wang, Lawrence K. (2009). Handbook of Advanced Industrial and Hazardous Wastes Treatment. Hoboken: CRC Press. ISBN 978-1-4200-7222-8. OCLC 664233915.
  12. Gillström, Peter (2006). Alternatives to pickling; preparation of carbon and low alloyed steel wire rod. Örebro, Sweden: Örebro universitetsbibliotek. p. 16. ISBN 9176684717. OCLC 185283772.
  13. Garverick, Linda (1994). Corrosion in the Petrochemical Industry. Materials Park, OH: ASM International. pp. 169–173. ISBN 9780871705051. OCLC 621873093.
This article is issued from Wikipedia. The text is licensed under Creative Commons - Attribution - Sharealike. Additional terms may apply for the media files.