Luting agent

https://archive.org/stream/dentalcosmos5619whit/dentalcosmos5619whit#page/33/mode/1up
This image taken from the Dental Cosmos shows a box of bottles containing dental cement which was used to lute dental crowns, bridges and inlays. It was produced by the L.D. Caulk Company in the early 1900s.

A luting agent is an application of a dental cement connecting the underlying tooth structure to a fixed prosthesis. To lute means to glue two different structures together. There are two major purposes of luting agents in dentistry – to secure a cast restoration in fixed prosthodontics (e.g. for use of retaining of an inlay, crowns, or bridges), and to keep orthodontic bands and appliances in situ.

In a complex restoration procedure, the selection of an appropriate luting agent is crucial to its long-term success.[1] In addition to preventing the fixed prosthesis from dislodging, it is also a seal, preventing bacteria from penetrating the tooth-restoration interface.[2]

Zinc phosphate is the oldest material available and has been used in dentistry for more than a century. The introduction of adhesive resin systems made a wide range of dental materials available as luting agents. The choice of luting agent is dependent on clinical factors including dental occlusion, tooth preparation, adequate moisture control, core material, supporting tooth structure, tooth location, etc.[3] Research has determined that no single luting agent is ideal for all applications.

Classification

There are many dental luting agents available. Recently introduced agents such as resins and resin-modified glass-ionomer cement (RMGIC) are claimed to perform better clinically that some traditional ones due to their improved properties.[1] Ultimately, the durability of restoration attached to the tooth surface using lutes depends on several factors, for instance strength of materials used, operator's skills, tooth type, and patient's behaviour.[4]

Dental lutes can be classified in many ways, some of which based on:

(i) user's knowledge and experience of use[5]

  • conventional: zinc phosphate, zinc polycarboxylate, and glass-ionomer (GI)
  • contemporary: resin-modified glass-ionomer cement (RMGIC) and resin

(ii) type of setting mechanism[6]

  • acid-base reaction: zinc phosphate, zinc polycarboxylate, glass-ionomer
  • polymerisation: resin-modified glass-ionomer cement (RMGIC) and resin

(iii) the expected duration of use of restoration[7]

  • definitive (long term): zinc phosphate, zinc polycarboxylate, glass-ionomer, resin-modified glass-ionomers (RMGIC) and resin
  • provisional (short term): eugenol, non-eugenol, resin, or polycarboxylate based

Definitive cements

Zinc Phosphate

This is the luting cement that has been about for the longest and has become very firmly established. It is still routinely used by almost one third of UK practitioners today.[8] It is usually made up of a powder (zinc oxide and magnesium oxide) and a liquid (aqueous phosphoric acid). Mixing of zinc phosphate is done by using a spatula to gradually incorporate the powder into the liquid. By using a chilled glass slab, the working time will be increased.[9]

Clinical studies have been carried out and results show that over a ten-year period, zinc phosphate cemented restorations had a lower risk of failure compared to other conventional cements such as glass ionomer or resin-modified glass ionomer.[10] However, it has some well-known clinical disadvantages including high clinical solubility, lack of adhesion, low setting pH[11] and a low tensile strength.

Zinc Polycarboxylate

Zinc polycarboxylate was the first cement to bind to tooth structure.[9] It is generally made up of the same powder as zinc phosphate (zinc oxide and up to 10% magnesium oxide) but uses a different liquid – aqueous copolymer of polyacrylic acid (30-40%).

It has a short working time which can make it difficult to use but this can be elongated by adding tartaric acid, mixing on a cold glass slab or using a lower powder: liquid ratio. In comparison with zinc phosphate, zinc polycarboxylate has been found to be distinctly superior in its adhesion to enamel and dentin under tensile loading.[12]

Glass Ionomer

This is the first of the GI luting cements to appear in 1978. It consists of fluoroaluminosilicate glass and a liquid containing polyacrylic acid, itaconic acid and water.[9] Alternatively, the acid may be freeze dried and added to powder with distilled water.

When in position it will release fluoride ions[11] which could have a potential anti caries effect. It also binds physicochemically to tooth structure and has a low coefficient of thermal expansion,[11] both of which are important to create a good seal and good retention. However, it has been linked with significant postoperative sensitivity.[13] It is also very initially acidic which may cause pulpal inflammation[14] and has a very slow setting reaction meaning hardening can take up to 7 days.

Resin cements

Resin cements are a type of polymerisable lutes. It consists of methacrylate and dimethacrylate monomers (e.g. bisphenol A-glycidyl methacrylate (Bis-GMA), urethane dimethacrylate (UDMA), tri-ethylene glycol dimethacrylate (TEGMA)), filler particles (e.g. quartz, fused silica, aluminosilicates and borosilicates) and an initiator which can be either chemically or light activated.[15]

  • Chemically/ self-cured resin cements

Autopolymerisation occurs once all the constituents are mixed together. External source of energy such as light and heat is not needed to activate the setting reaction. Excess cement should be removed immediately after seating the restoration by using interproximal dental instruments such as dental floss. Autopolymerised cement is proved to be the most radiolucent among all resin cements,[11] making it relatively difficult to be seen on radiographs.

  • This photo shows an operator using a dental curing light to initiate the setting reaction of the dental cement used.
    Light-cured resin cements[1]

Due to the presence of light-activated components (photo-initiators), this type of resin cement requires an external light source to initiate the setting reaction. This characteristic allows command set at the periphery of the restoration where light can reach the cement. However, this type of cement is not suitable for thick restorations due to attenuation of light. Instead, a chemically-cured resin cement should be used.

  • Dual-cured resin cements

It consists of a light-activated paste mixed with a chemical catalyst for resin polymerisation. It is widely used for luting dental restoration whereby the thickness allows penetration of light for partial curing only. On the other hand, the chemically-cured component is key in ensuring complete polymerisation and hence full strength acquisition.[16] Discolouration may occur due to the presence of aromatic amine.[17] Overall, the combination of its physical and chemical properties makes it the most favourable type.[11]

Today resin cements are manufactured in different shades to accommodate the demanding aesthetic needs.[1] It is also well known for its high flexural strength, which ranges from 64 to 97 MPa.[11] Although it has the advantage of attaching restorations with minimal retentive capacity to tooth surfaces due to its high bond strength to dentine, its methacrylate constituent causes it to undergo polymerisation shrinkage when setting.[16] The strain introduced by the shrinkage will tend to raise the tensile stresses significantly at areas where the cement is thick. However, the cement thickness usually used is sufficiently low to raise concern.[18] Another way to look at the strain applied onto the tooth structure is to consider the configuration factor (C-factor) of the lute, especially in the case of inlay type restoration.[16] The use of resin cements is considered technique sensitive as compared to conventional cements because it requires multiple steps for bonding and is difficult to clean up.[1]

Resin-modified glass-ionomer cement (RMGIC)

RMGIC, also known as hybrid cements, was developed with the purpose of eliminating weaknesses of the traditional glass-ionomer (GI) to enhance its existing properties.[19] The addition of polymerisable resins (hydrophilic methacrylate monomers) results in higher compressive and tensile strength, as well as lower solubility,[1] all of which are ideal properties of a dental luting agent. The setting reaction takes place with the relatively quick polymerisation of resins and gradual acid-base reaction of GI.[1] At the early stage of setting reaction, RMGIC has a certain degree of solubility at the margins. Therefore, it is important to keep the margin dry for around 10 minutes to minimise loss of marginal cement.[1]

Theoretically, RMGIC benefits the teeth by releasing fluoride at the marginal area to reduce the risk of tooth decay. However, there is currently no clinical evidence to prove this[16] since the cement film is very thin (only 20–30μm) at the margin.[9]

This photo shows the application of luting cement onto a temporary dental crown. The use of lute in this case is therefore considered provisional because of the short duration of use of the crown (up to 6 weeks). The crown will eventually be replaced by a permanent crown.

Provisional/Temporary cements

Provisional (or temporary) luting agents are used specifically for inter-appointment fixation of temporary restorations, prior to cementation of a permanent restoration.[20] It is mainly provisional crowns and bridges (fixed partial dentures) that are cemented with eugenol-containing temporary cements, but sometimes they may be used for permanent restorations.[21]

As these temporary restorations will require removal, their ideal properties should consist of poor physical properties, such as low tensile strength and high solubility; as well as no pulp irritability and easy handling. The main examples of temporary luting agents include zinc oxide-eugenol cements, non-eugenol containing zinc oxide cements and calcium hydroxide pastes.[1]

Zinc oxide-eugenol

Eugenol (4-allyl-2-methoxy phenol) is the principal constituent of clove oil, and when mixed with zinc oxide leads to a chelating reaction. All eugenol reacts to zinc oxide eugenol, meaning none is available to diffuse once setting is complete. Supposedly its therapeutic effects are supported by dentinal tubule fluid promoting the release of eugenol and its penetration towards the pulp.[22]

Zinc oxide-eugenol is often found as a two-paste material when used for temporary cementation. The paste containing zinc oxide often includes mineral or vegetable oils, and the eugenol has fillers incorporated into it to form the other paste.[1] A well-known product utilised in the two-paste form is Temp-Bond™.

Zinc oxide-eugenol may present as a powder (zinc oxide) that requires mixing with a liquid (eugenol). The zinc oxide powder may contain up to 8% of other zinc salts (acetate, propionate, or succinate) as accelerators. The liquid containing eugenol has up to 2% of acetic acid added as an accelerator.[1] A well-known product utilised in this powder-liquid form is Kalzinol™.

Zinc oxide non-eugenol

If cementation of a definitive restoration would require a resin-based luting agent, there is evidence indicating the use of a zinc oxide non-eugenol containing cement. Non-eugenol materials use long chain aliphatic acids or aryl-substituted butyric acid to react with zinc oxide particles.[1] Eugenol itself is known to be incompatible with resin polymers,[23] as it is a radical scavenger (like other phenolic compounds) and therefore inhibits polymerisation of resin materials.[24][25]

Further evidence illustrated that the application of eugenol-containing cement to cured composite resin cores before final cementation with resin cement significantly reduced retention of the crowns.[26] It is also worth bearing in mind that a temporary cement's incomplete removal from a cured resin composite core may affect the final restoration's cementation quality.[26] A well-known product used in this instance is Temp-Bond NE™.

Clinical applications

Cements can either be permanent (called definitive) or temporary (called provisional):

Definitive cements

Zinc phosphate

This image shows the different types of indirect restorations mentioned in the clinical application section. The ideal luting agent is chosen depending on the type of materials used to fabricate the restoration.
  • Zinc phosphate is used to place metal constructed restorations which are mechanically retentive.[16] The material is also suitable for cementing prefabricated or cast metal post-cores.[27] It can also be used to lute long span bridges.[1]
  • The use of zinc phosphate in luting a porcelain crown may result in decreased aesthetic properties due to the high concentrations of unreacted zinc oxide, especially if the cement lute margin is visible. To avoid this, the crown margins should be kept within gingival crevice, so that the cement lute remains hidden.[23]

Zinc polycarboxylate

  • This material is mainly used in attaching crowns and inlays.[23] Due to masticatory forces causing deformation, it can only be used in short-span bridges.[1] Zinc polycarboxylate is adherent to tooth structure such as enamel and dentine, but has weak or no bond with gold and porcelain. This presents limited use when it comes to luting gold or porcelain crowns. However, zinc polycarboxylate bonds to non-precious metal alloys that have been increasingly used in porcelain fused to metal (PFM) crowns.[23]
  • Zinc polycarboxylate bonds well with stainless steel, and this makes it useful for the attachment of orthodontic bands.[23]
  • As a result of a high concentration of unreacted zinc oxide cores, zinc polycarboxylate sets opaque. If used in porcelain crowns, this will degrade the aesthetic properties of the restoration if the cement lute is left visible.[23]

Glass ionomer

  • Glass ionomer cement when combined with retentive preparations produced a high retentive strength when used as a cement for metal copings to uremic teeth.[28]
  • Glass ionomer cements can be used with metal and metal-ceramic restorations provided they possess adequate retentive and resistance form.6 They are however, contraindicated for all-ceramic restorations that are low-strength.[9]
  • It is also suitable for use in amalgam restorations, due to its ability to withstand amalgam condensation. It has been said that GI cements can give more rigid support compared to calcium hydroxide cements, making it popular as a lining material.[23]
  • Glass ionomer has an aesthetic advantage over zinc phosphate and zinc polycarboxylate when it comes to luting porcelain crowns.[23] This is because of the presence of unreacted cores of glass rather than zinc oxide, therefore making it more translucent.[23] However, improvements are still required to achieve a true match to porcelain.[23]
  • Glass ionomer has not been recommended for cementing posts, as the vibration caused by tooth preparation may decrease the retention provided by the cement.[1]
  • In orthodontics, glass ionomer cements are widely used to attach orthodontic bands. The presence of an adhesive seal between the cement and tooth structure additional to fluoride release can help to maintain teeth in good condition throughout orthodontic treatment. However, in practice, the high rate of brackets debonding during treatment has shown that glass ionomer is not a suitable material in this aspect.[23]

Resin modified glass ionomer

  • RMGIC has demonstrated a successful history when used for both metal and metal ceramic restorations[29] The cement also demonstrated good results with metal and composite fibre posts.[26] However, they do not provide adequate retention when used on tooth preparations with poor retention and resistance forms.[1]
  • Due to the possibility of hygroscopic expansion, these cements are not recommended for use with all-ceramic restorations that are susceptible to etching and with posts.[30]
  • Similar to the Glass ionomer cement, RMGIC can also be used to provide a high retentive strength when used in cementation of metal copings on uremic teeth with retentive preparations.[28]

Resin

  • Resin cements are widely selected for luting non-metallic restorations, resin bonded bridges, ceramic crowns and porcelain veneers.[26] They are available in a different number of shades, viscosities and aesthetic try-in pastes. These cements are also an option for use with ceramic and resin composite inlays and onlays.[26]
  • They also demonstrated a favourable outcome when used for all-ceramic restorations, veneers, metal or metal-ceramic restorations with compromised retention and resistance form.[31]
  • Resin cement is also shown to be useful for cementation of post in endodontically treated teeth.[31]

Self-adhesive cements

  • Self-adhesive cements do not require intermediate steps to bond tooth structure, unlike resin cements.[26] This gives simplicity and efficiency in its use. They are dual-cured and are most effective when bonded to dentine.[26] It is suitable for cementing all-ceramic crowns, porcelain inlays and onlays.[26]
  • Self-adhesive resin cements such as RelyX Unicem (3M ESPE) has shown an acceptable clinical result when used for ceramic inlays.[32][33]
  • Self-adhesive resin cements also demonstrated high and adequate survival rates when used as a cement for metal ceramic crowns making it a feasible alternative.[34][16]

Provisional cements

Zinc oxide eugenol

  • Zinc oxide eugenol is used for luting temporary restorations due to its good sealing abilities but inferior physical properties.[1]
  • Eugenol containing cements should be used with caution as the eugenol can contaminate the preparation by inhibiting the polymerization of certain resin based composites which are used as a definitive filling material.[35] They also reduce the bond strength of both total and self-etching adhesive systems to dentin if used before an indirect bonding restoration.[36]
  • Another report shows that there is no difference in bond strengths of self-adhesive resin cements to dentine between prior application of eugenol free and eugenol containing provisional cements.[37]
  • Later publications show a reduction in luting agent bond strengths to dentine when eugenol containing provisional cements are used. Nevertheless, contamination of dentine which interference with adhesion of definitive luting agent is inevitable when a provisional cement is used regardless of whether the cement contains eugenol or not.[7]

Selection of luting agent to be used for a given restoration should be based on a basic knowledge of the materials available, the type of restoration to be placed, the requirements of the patient and the expertise and experience of the clinician.

Summary properties of cements

Type of luting agents Examples Constituents Properties Advantages Disadvantages
Definitive Cements Zinc phosphate cements Fleck's Zinc Phosphate Cement (Mizzy, Cherry Hill, NJ, USA) Zinc oxide powder + magnesium oxide (2-10%) + phosphoric acid (45-64%)
  • Non-adhesive solely mechanical retention
  • Acidic
  • Reasonable working time
  • High early strength
  • Good compressive strength
  • Irritant to pulp (low pH)
  • High solubility (very soluble in its non-matured state[38])
  • Low tensile strength (brittle)
Polycarboxylate cements Poly F Plus (Dentsply) Zinc oxide powder + polyacrylic acid (30-40%)
  • Pseudoplastic
  • Antibacterial properties
  • Adhesive to enamel, dentine, some metals
  • Higher tensile strength[38]
  • Less irritant to pulp (low pH but less penetration to pulp due to high molecular weight
  • Adequate resistance to water dissolution[39]
  • Short working time
  • Low compressive strength
  • Not resistant to acid dissolution[39]
Glass polyalkenoate cements Aquacem (Dentsply) Fluoroaluminosilicate glass + acrylic acid or of a maleic/acrylic acid copolymer +Tartaric acid
  • High early solubility[38]
  • Coefficient of thermal expansion similar to tooth
  • Cariostatic potential (fluoride release)
  • Translucent (can be used for porcelain crowns)[39]
  • Tooth sensitivity after restoration delivery[38]
  • Susceptible to moisture contamination during 1st few hours of placement
Resin modified glass polyalkenoate cements and compomers RelyX Luting Cement (3M ESPE) Glass ionomer + resin monomer
  • Improved biocompatibility
  • Cariostatic potential (fluoride release)
  • Compressive strength, diametral tensile strength and flexural strength improved compared to zinc phosphate/zinc polycarboxylate/glass ionomer but less than composites[39]
  • Easy manipulation and use
  • Fluoride release as GIC
  • Reduced solubility as compared to GIC
  • High bond strength to moist dentine
  • Hygroscopic expansion, so avoid under conventional all ceramic crowns
Chemically adhesive resin luting cements
  • Panavia F (Kuraray Dental)
  • RelyX ARC (3M ESPE)
 Derive from resin composites with the active constituent being either 4-META (4-methacryloxyethyl

trimellitate anhydride)

or MDP (10-

methacryloyloxydecyldihydrogenphosphate)
  • Adhesively bonded to metal-based restorations
  • Difficult to retrieve metal-based crowns cemented
Resin luting cements RelyX Unicem
  • Adhesive luting with ceramic restorations
  • Self-adhesive (etch and bond)
  • High compressive[38]
  • Tensile strength[38]
  • Low solubility[38]
  • Good aesthetic properties
  • Does not bond chemically to metal
  • Difficult excess removal of cement[38]
  • Technique sensitive[38]
Provisional Cements Zinc oxide eugenol provisional cement TempBond (Kerr) Two-paste material (eugenol, zinc oxide)
  • setting time reduces with increase with temperature[38]
  • good sealing ability
  • low tensile strength/compressive strength/solubility
  • eugenol interferes with polymerisation of resin composite
Zinc oxide non-eugenol provisional cement Temp-Bond NE™ Long chain aliphatic acids/aryl-substituted butyric acid, zinc oxide particles
  • satisfactorily seal and retain well-fitting provisional restorations[38]
  • toxic if placed near pulp tissue
Resin provisional

(very little independent research has been conducted)
  • TempBond Clear (Kerr)
  • Sensitemp (Sultan, Hackensack, NJ, USA)
  • Temporary Resin Cement (Mizzy, Cherry Hill, NJ, USA)[38]

References

  1. 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 Lad PP, Kamath M, Tarale K, Kusugal PB (February 2014). "Practical clinical considerations of luting cements: A review". Journal of International Oral Health. 6 (1): 116–20. PMC 3959149. PMID 24653615.
  2. ↑ Pameijer CH, Glantz PO, von Fraunhofer A (2012). "Clinical and technical considerations of luting agents for fixed prosthodontics". International Journal of Dentistry. 2012: 565303. doi:10.1155/2012/565303. PMC 3389718. PMID 22792107.
  3. ↑ Özcan M (2013). "Luting cements for dental applications". Non-Metallic Biomaterials for Tooth Repair and Replacement. pp. 375–394. doi:10.1533/9780857096432.3.375. ISBN 9780857092441.
  4. ↑ Demarco FF, Corrêa MB, Cenci MS, Moraes RR, Opdam NJ (January 2012). "Longevity of posterior composite restorations: not only a matter of materials". Dental Materials. 28 (1): 87–101. doi:10.1016/j.dental.2011.09.003. PMID 22192253.
  5. ↑ Donovan TE, Cho GC (March 1999). "Contemporary evaluation of dental cements". Compendium of Continuing Education in Dentistry. 20 (3): 197–9, 202–8, 210 passim, quiz 220. PMID 11692331.
  6. ↑ AD Wilson, JW Nicholson. Acid-base cements, their biomedical and industrial applications. New York:Cambridge University Press. 1993:1–383.
  7. 1 2 Pameijer CH (2012). "A review of luting agents". International Journal of Dentistry. 2012: 752861. doi:10.1155/2012/752861. PMC 3296365. PMID 22505909.
  8. ↑ McKenna JE, Ray NJ, McKenna G, Burke FM (2011). "The effect of variability in the powder/liquid ratio on the strength of zinc phosphate cement". International Journal of Dentistry. 2011: 679315. doi:10.1155/2011/679315. PMC 3235453. PMID 22190935.
  9. 1 2 3 4 5 Burgess JO, Ghuman T (June 2008). "A practical guide to the use of luting cement" (PDF). Dental Academy of Continuing Education.
  10. ↑ Behr M, Rosentritt M, Wimmer J, Lang R, Kolbeck C, Bürgers R, Handel G (May 2009). "Self-adhesive resin cement versus zinc phosphate luting material: a prospective clinical trial begun 2003". Dental Materials. 25 (5): 601–4. doi:10.1016/j.dental.2008.11.003. PMID 19100611.
  11. 1 2 3 4 5 6 Attar N, Tam LE, McComb D (February 2003). "Mechanical and physical properties of contemporary dental luting agents". The Journal of Prosthetic Dentistry. 89 (2): 127–34. doi:10.1067/mpr.2003.20. PMID 12616231.
  12. ↑ Phillips RW, Swartz ML, Rhodes B (1970). "An evaluation of a carboxylate adhesive cement". Journal of the American Dental Association. 81 (6): 1353–9. doi:10.14219/jada.archive.1970.0390. PMID 5273600.
  13. ↑ Author, UTHSCSA Dental School CATs. "UTCAT2686, Found CAT view, CRITICALLY APPRAISED TOPICs". cats.uthscsa.edu. Retrieved 2018-01-18. {{cite web}}: |last= has generic name (help)
  14. ↑ Smith DC, Ruse ND (1986). "Acidity of glass ionomer cements during setting and its relation to pulp sensitivity". Journal of the American Dental Association. 112 (5): 654–7. doi:10.14219/jada.archive.1986.0069. PMID 3458784.
  15. ↑ McCabe JF, Walls AW (2008). Applied Dental Materials (9th ed.). Oxford, UK: Blackwell Publishing. ISBN 978-1-4051-3961-8.
  16. 1 2 3 4 5 6 Piwowarczyk A, Schick K, Lauer HC (June 2012). "Metal-ceramic crowns cemented with two luting agents: short-term results of a prospective clinical study". Clinical Oral Investigations. 16 (3): 917–22. doi:10.1007/s00784-011-0580-5. PMID 21681387.
  17. ↑ GJ Christensen. Reducing the confusion about resin cements. Clin Rep. 2008;1:1–3.
  18. ↑ May LG, Kelly JR (October 2013). "Influence of resin cement polymerization shrinkage on stresses in porcelain crowns". Dental Materials. 29 (10): 1073–9. doi:10.1016/j.dental.2013.07.018. PMID 23973087.
  19. ↑ Sunico-Segarra M, Segarra A (2014-10-13). A practical clinical guide to resin cements. Berlin. ISBN 978-3662438428. OCLC 894046576.
  20. ↑ Sakaguchi RL, Powers JM (2012). Craig's restorative dental materials (13th ed.). St. Louis, Mo.: Elsevier/Mosby. ISBN 9780323081085. OCLC 757994720.
  21. ↑ Bayindir F, Akyil MS, Bayindir YZ (December 2003). "Effect of eugenol and non-eugenol containing temporary cement on permanent cement retention and microhardness of cured composite resin". Dental Materials Journal. 22 (4): 592–9. doi:10.4012/dmj.22.592. PMID 15005235.
  22. ↑ Ganss C, Jung M (March 1998). "Effect of eugenol-containing temporary cements on bond strength of composite to dentin". Operative Dentistry. 23 (2): 55–62. PMID 9573789.
  23. 1 2 3 4 5 6 7 8 9 10 11 McCabe JF, Walls A (2008). Applied dental materials. Walls, Angus. (9th ed.). Oxford, UK: Blackwell Pub. ISBN 978-1405139618. OCLC 180080871.
  24. ↑ Taira J, Ikemoto T, Yoneya T, Hagi A, Murakami A, Makino K (1992). "Essential oil phenyl propanoids. Useful as .OH scavengers?". Free Radical Research Communications. 16 (3): 197–204. doi:10.3109/10715769209049172. PMID 1318253.
  25. ↑ Marshall SJ, Marshall GW, Harcourt JK (October 1982). "The influence of various cavity bases on the micro-hardness of composites". Australian Dental Journal. 27 (5): 291–5. doi:10.1111/j.1834-7819.1982.tb05249.x. PMID 6962692.
  26. 1 2 3 4 5 6 7 8 Millstein PL, Nathanson D (June 1992). "Effects of temporary cementation on permanent cement retention to composite resin cores". The Journal of Prosthetic Dentistry. 67 (6): 856–9. doi:10.1016/0022-3913(92)90601-6. PMID 1403878.
  27. ↑ Habib B, von Fraunhofer JA, Driscoll CF (September 2005). "Comparison of two luting agents used for the retention of cast dowel and cores". Journal of Prosthodontics. 14 (3): 164–9. doi:10.1111/j.1532-849X.2005.00349.x. PMID 16336233.
  28. 1 2 Ghazy MH, Aboumadina MM, Mahmoud SH (May 2014). "Retentiveness of metal coping luted to teeth of uremic patients undergoing hemodialysis using five different luting cements". Operative Dentistry. 39 (3): E101–8. doi:10.2341/12-523-LR2. PMID 24191870.
  29. ↑ Leevailoj C, Platt JA, Cochran MA, Moore BK (December 1998). "In vitro study of fracture incidence and compressive fracture load of all-ceramic crowns cemented with resin-modified glass ionomer and other luting agents". The Journal of Prosthetic Dentistry. 80 (6): 699–707. doi:10.1016/s0022-3913(98)70058-7. PMID 9830076.
  30. ↑ Mount GJ (2003). An atlas of glass-ionomer cements : a clinician's guide (3rd ed.). London: Martin Dunitz. ISBN 978-1841840697. OCLC 53373473.
  31. 1 2 Pegoraro TA, da Silva NR, Carvalho RM (April 2007). "Cements for use in esthetic dentistry". Dental Clinics of North America. 51 (2): 453–71, x. doi:10.1016/j.cden.2007.02.003. PMID 17532922.
  32. ↑ Swift EJ (August 2012). "Critical appraisal. Self-adhesive resin cements--part II". Journal of Esthetic and Restorative Dentistry. 24 (4): 287–91. doi:10.1111/j.1708-8240.2012.00524.x. PMID 22863137.
  33. ↑ Peumans M, De Munck J, Van Landuyt K, Poitevin A, Lambrechts P, Van Meerbeek B (April 2010). "Two-year clinical evaluation of a self-adhesive luting agent for ceramic inlays". The Journal of Adhesive Dentistry. 12 (2): 151–61. doi:10.3290/j.jad.a17547. PMID 20157666.
  34. ↑ Brondani LP, Pereira-Cenci T, Wandsher VF, Pereira GK, Valandro LF, Bergoli CD (April 2017). "Longevity of metal-ceramic crowns cemented with self-adhesive resin cement: a prospective clinical study". Brazilian Oral Research. 31: e22. doi:10.1590/1807-3107BOR-2017.vol31.0022. PMID 28403329.
  35. ↑ Hotz P, Schlatter D, Lussi A (1992). "[The modification of the polymerization of composite materials by eugenol-containing temporary fillings]". Schweizer Monatsschrift für Zahnmedizin = Revue Mensuelle Suisse d'Odonto-Stomatologie = Rivista Mensile Svizzera di Odontologia e Stomatologia. 102 (12): 1461–6. PMID 1475669.
  36. ↑ Ribeiro JC, Coelho PG, Janal MN, Silva NR, Monteiro AJ, Fernandes CA (March 2011). "The influence of temporary cements on dental adhesive systems for luting cementation". Journal of Dentistry. 39 (3): 255–62. doi:10.1016/j.jdent.2011.01.004. PMID 21241765.
  37. ↑ Bagis B, Bagis YH, Hasanreisoğlu U (December 2011). "Bonding effectiveness of a self-adhesive resin-based luting cement to dentin after provisional cement contamination". The Journal of Adhesive Dentistry. 13 (6): 543–50. doi:10.3290/j.jad.a19811. PMID 21246076.
  38. 1 2 3 4 5 6 7 8 9 10 11 12 Hill EE, Lott J (June 2011). "A clinically focused discussion of luting materials". Australian Dental Journal. 56 Suppl 1: 67–76. doi:10.1111/j.1834-7819.2010.01297.x. PMID 21564117.
  39. 1 2 3 4 Ladha K, Verma M (June 2010). "Conventional and contemporary luting cements: an overview". Journal of Indian Prosthodontic Society. 10 (2): 79–88. doi:10.1007/s13191-010-0022-0. PMC 3081255. PMID 21629449.
This article is issued from Offline. The text is licensed under Creative Commons - Attribution - Sharealike. Additional terms may apply for the media files.