Group 6 element

Chromium was first reported on July 26, 1761, when Johann Gottlob Lehmann found an orange-red mineral in the Beryozovskoye mines in the Ural Mountains of Russia, which he named "Siberian red lead," which was found out in less than 10 years to be a bright yellow pigment.[1] Though misidentified as a lead compound with selenium and iron components, the mineral was crocoite with a formula of PbCrO₄.[1] Studying the mineral in 1797, Louis Nicolas Vauquelin produced chromium trioxide by mixing crocoite with hydrochloric acid, and metallic chromium by heating the oxide in a charcoal oven a year later.[2] He was also able to detect traces of chromium in precious gemstones, such as ruby or emerald.[1][3]

Molybdenite—the principal ore from which molybdenum is now extracted—was previously known as molybdena, which was confused with and often implemented as though it were graphite. Like graphite, molybdenite can be used to blacken a surface or as a solid lubricant.[4] Even when molybdena was distinguishable from graphite, it was still confused with a galena (a common lead ore), which took its name from Ancient Greek Μόλυβδος molybdos, meaning lead.[5] It was not until 1778 that Swedish chemist Carl Wilhelm Scheele realized that molybdena was neither graphite nor lead.[6][7] He and other chemists then correctly assumed that it was the ore of a distinct new element, named molybdenum for the mineral in which it was discovered. Peter Jacob Hjelm successfully isolated molybdenum by using carbon and linseed oil in 1781.[5][8]

Regarding tungsten, in 1781 Carl Wilhelm Scheele discovered that a new acid, tungstic acid, could be made from scheelite (at the time named tungsten). Scheele and Torbern Bergman suggested that it might be possible to obtain a new metal by reducing this acid.[9] In 1783, José and Fausto Elhuyar found an acid made from wolframite that was identical to tungstic acid. Later that year, in Spain, the brothers succeeded in isolating tungsten by reduction of this acid with charcoal, and they are credited with the discovery of the element.[10][11]

Seaborgium was first produced by a team of scientists led by Albert Ghiorso who worked at the Lawrence Berkeley Laboratory in Berkeley, California, in 1974. They created seaborgium by bombarding atoms of californium-249 with ions of oxygen-18 until seaborgium-263 was produced.

During the 1800s, chromium was primarily used as a component of paints and in tanning salts. At first, crocoite from Russia was the main source, but in 1827, a larger chromite deposit was discovered near Baltimore, United States. This made the United States the largest producer of chromium products until 1848 when large deposits of chromite where found near Bursa, Turkey.[12] Chromium was used for electroplating as early as 1848, but this use only became widespread with the development of an improved process in 1924.[13]

For about a century after its isolation, molybdenum had no industrial use, owing to its relative scarcity, difficulty extracting the pure metal, and the immaturity of the metallurgical subfield.[14][15][16] Early molybdenum steel alloys showed great promise in their increased hardness, but efforts were hampered by inconsistent results and a tendency toward brittleness and recrystallization. In 1906, William D. Coolidge filed a patent for rendering molybdenum ductile, leading to its use as a heating element for high-temperature furnaces and as a support for tungsten-filament light bulbs; oxide formation and degradation require that moly be physically sealed or held in an inert gas. In 1913, Frank E. Elmore developed a flotation process to recover molybdenite from ores; flotation remains the primary isolation process. During the first World War, demand for molybdenum spiked; it was used both in armor plating and as a substitute for tungsten in high-speed steels. Some British tanks were protected by 75 mm (3 in) manganese steel plating, but this proved to be ineffective. The manganese steel plates were replaced with 25 mm (1 in) molybdenum-steel plating allowing for higher speed, greater maneuverability, and better protection.[5] After the war, demand plummeted until metallurgical advances allowed extensive development of peacetime applications. In World War II, molybdenum again saw strategic importance as a substitute for tungsten in steel alloys.[17]

In World War II, tungsten played a significant role in background political dealings. Portugal, as the main European source of the element, was put under pressure from both sides, because of its deposits of wolframite ore at Panasqueira. Tungsten's resistance to high temperatures and its strengthening of alloys made it an important raw material for the arms industry.[18]