Sandpaper

Sandpaper and glasspaper are names used for a type of coated abrasive that consists of sheets of paper or cloth with abrasive material glued to one face.

Sheets of sandpaper with different grit sizes (40 (coarse), 80, 150, 240, 600 (fine)).

There are many varieties of sandpaper, with variations in the paper or backing, the material used for the grit, grit size, and the bond.

In the modern manufacture of these products, sand and glass have been replaced by other abrasives such as aluminium oxide or silicon carbide. It is common to use the name of the abrasive when describing the paper, e.g. "aluminium oxide paper", or "silicon carbide paper".

Sandpaper is produced in a range of grit sizes and is used to remove material from surfaces, whether to make them smoother (for example, in painting and wood finishing), to remove a layer of material (such as old paint), or sometimes to make the surface rougher (for example, as a preparation for gluing). The grit size of sandpaper is usually stated as a number that is inversely related to the particle size. A small number such as 20 or 40 indicates a coarse grit, while a large number such as 1500 indicates a fine grit.

History

The first recorded instance of sandpaper was in 13th-century China when crushed shells, seeds, and sand were bonded to parchment using natural gum.[1][2]

Shark skin (placoid scales) has also been used as an abrasive, and the rough scales of the Coelacanth are used for the same purpose by the natives of Comoros.[3] Boiled and dried, the rough horsetail plant is used in Japan as a traditional polishing material, finer than sandpaper.

Glass paper was manufactured in London in 1833 by John Oakey, whose company had developed new adhesive techniques and processes, enabling mass production. Glass frit has sharp-edged particles and cuts well whereas sand grains are smoothed down and do not work well as an abrasive. Cheap sandpaper was often passed off as glass paper; Stalker and Parker cautioned against it in A Treatise of Japaning and Varnishing published in 1688.[4]

In 1921, 3M invented a sandpaper with silicon carbide grit and a waterproof adhesive and backing, known as Wet and dry. This allowed use with water, which would serve as a lubricant to carry away particles that would otherwise clog the grit. Its first application was in automotive paint refinishing.[5]

Coated abrasive

Assorted coated abrasives

A coated abrasive is an abrasive grain bonded to a flexible substrate using adhesives.[6] Common substrates are paper, cloth, vulcanized fiber, and plastic films and come in grit sizes range from very coarse (~2 mm) to ultrafine (submicrometre). The international standard for coated abrasives is ISO 6344. Sandpaper and emery cloth are coated abrasives for hand use, usually non-precision. Other coated abrasive forms include sanding cords, pads, belts, and discs. Variants are available for use by hand or as components for power tools such as sanders, die grinders and belt sanders.

Mounting systems

Examples of a quick change mounting system

A quick change system is commonly used with disc type coated abrasives. A plastic or metal hub is bonded to one of the faces, which is threaded. This then mates directly to the sander/grinder or to a mandrel that can be mounted in a sander, grinder, or drill. The advantage is that the disc can be quickly replaced when needed. Quick change discs range in sizes from 50 millimetres (2.0 in) to no upper limit.

Backing

320 grit silicon carbide sandpaper, with close-up view

In addition to paper, backing for sandpaper includes cloth (cotton, polyester, rayon), PET film, "fibre", and rubber. Cloth backing is used for sandpaper discs and belts, while mylar is used as backing for extremely fine grits. Fibre or vulcanized fibre is a strong backing material consisting of many layers of polymer impregnated paper. The weight of the backing is usually designated by a letter. For paper backings, the weight ratings range from "A" to "F", with A designating the lightest and F the heaviest. Letter nomenclature follows a different system for cloth backings, with the weight of the backing rated J, X, Y, T, and M, from lightest to heaviest. A flexible backing allows sandpaper to follow irregular contours of a workpiece; relatively inflexible backing is optimal for regular rounded or flat surfaces. Sandpaper backings may be glued to the paper or form a separate support structure for moving sandpaper, such as used in sanding belts and discs. Stronger paper or backing increases the ease of sanding wood. The harder the backing material, the faster the sanding, the faster the wear of the paper and the rougher the sanded surface.

Abrasives

Emery cloth sheet whose component abrasive is aluminium oxide

Types of abrasive materials include:

  • Glass: No longer commonly used.
  • Flint: No longer commonly used.
  • Garnet: Commonly used in woodworking.
  • Emery: Commonly used to abrade or polish metals.
  • Aluminium oxide: The most common in modern use, with the widest variety of grits, lowest unit cost; can be used on metal (i.e. body shops) or wood.
  • Silicon carbide: Available in very coarse grits all the way through to microgrits, common in wet applications.
  • Alumina-zirconia: (An aluminium oxide–zirconium oxide alloy), used for machine grinding applications.
  • Chromium(III) oxide: Used in extremely fine micron grit (micrometre level) papers.
  • Diamond: Used for finishing and polishing hard metals, ceramics and glass.
  • Ceramic aluminium oxide: Used in high pressure applications, used in both coated abrasives, as well as in bonded abrasives.

Sandpaper may be "stearated" where a dry lubricant is loaded to the abrasive. Stearated papers are useful in sanding coats of finish and paint as the stearate "soap" prevents clogging and increases the useful life of the sandpaper.

The harder the grit material, the easier the sanding of harder surfaces like hardwoods such as hickory, pecan, or wenge. The grit material for polishing granite must be harder than granite.

Bonds

Different adhesives are used to bond the abrasive to the paper. Hide glue is still used, but this glue often cannot withstand the heat generated during machine sanding and is not waterproof. Waterproof sandpapers or wet/dry sandpapers use a resin bond and a waterproof backing.

Sandpaper can be either closed coat or open coat.[7] Approximately 90% to 95% of the surface is covered with abrasive grains with a closed coat. Closed coat sandpaper is good for hand sanding or working with harder materials. In comparison, 50% to 70% of the surface is covered with abrasive grains with open coat sandpaper. The separation between particles makes the sandpaper more flexible, which prevents the sandpaper from clogging. However, the gaps in grit coverage limits the sandpaper's ability to perform even polishing jobs. Open coat sandpaper is better for softer materials.

Wet and dry sandpaper is more effective used wet because clogging is reduced by particles washing away from the grinding surface.[8]

Shapes

Sandpaper comes in a number of different shapes and sizes:

  • sheet: usually 9 by 11 inches (23 by 28 cm), but other sizes may be available
  • belt: usually cloth backed, comes in different sizes to fit different belt sanders.
  • disk: made to fit different models of disc and random orbit sanders. May be perforated for some models of sanders. Attachment includes pressure-sensitive adhesive (PSA) and "hook-and-loop" (similar to Velcro).
  • rolls: known as "shag rolls" by many contractors
  • sponge: for tight places

Grit sizes

Grit sizes

Grit size refers to the size of the particles of abrading materials embedded in the sandpaper. These measurements are determined by the amount of the abrasive material that can fit through a square inch filter.[9] Several standards have been established for grit size. These standards establish not only the average grit size, but also the allowable variation from the average. The two most common are the United States CAMI (Coated Abrasive Manufacturers Institute, now part of the Unified Abrasives Manufacturer's Association) and the European FEPA (Federation of European Producers of Abrasives) "P" grade. The FEPA system is the same as the ISO 6344 standard. Other systems used in sandpaper include the Japanese Industrial Standards Committee (JIS), the micron grade (generally used for very fine grits). Cheaper sandpapers may sometimes only use descriptive nomenclature such as "coarse", "medium" and "fine" without referring to any standard.

The following table, compiled from the references at the bottom, compares the CAMI and "P" designations with the average grit size in micrometres (µm).

Grit size table
ISO/FEPA Grit designation CAMI Grit designation Average particle diameter (µm)
Macrogrits
Extra Coarse (Very fast removal of material, hardwood flooring initial sanding) P12 1815
P16 1324
P20 1000
P24 764
24 708
P30 642
30 632
P36 538
36 530
Coarse (Rapid removal of material) P40 40 425
50 348
P50 336
Medium (for sanding bare wood in preparation for finishing, gentle removal of varnish, and skateboard grip tape) 60 265
P60 269
P80 201
80 190
Fine (sanding bare wood in preparation for finishing, not suitable for removing varnish or paint from wood, use for cleaning plaster and water stain from wood) P100 162
100 140
P120 125
120 115
Very Fine (sanding of bare wood) P150 100
150 92
P180 180 82
P220 220 68
Microgrits
Very Fine (sanding finishes between coats) P240 58.5
240 53.0
P280 52.2
P320 46.2
P360 40.5
Extra fine, start polishing of wood 320 36.0
P400 35.0
P500 30.2
360 28.0
P600 25.8
Super fine (final sanding of finishes, final sanding of wood) 400 23.0
P800 21.8
500 20.0
P1000 18.3
600 16.0
P1200 15.3
Ultra fine (final sanding and polishing of thick finishes) P1500 800 12.6
P2000 1000 10.3
P2500 8.4

Emery cloth

320 grit emery cloth

Emery cloth is a type of coated abrasive that has emery glued to a cloth backing. It is used for hand metalworking. It may be sold in sheets or in narrow rolls, typically 25 or 50 mm wide, often described as "emery tape". The cloth backing makes emery cloth stronger in tension than paper, but still allows a sheet to be conveniently torn to size. Emery (largely displaced by improved products such as aluminium oxide and silicon carbide) is used for scrubbing highly abraded and rough surfaces to a smooth and shiny finish, notably in watchmaking.[10] Emery paper, more commonly seen, has a paper backing and is usually a finer grit.

Emery was considered a suitable abrasive for fitting work and the final adjustment of steel parts for a perfect fit. It had the advantage that, unlike harder abrasives, it was not considered to embed abrasive traces in the polished components afterwards. Emery was also used for cleaning, as a means of removing rust from polished steel components.

Both emery cloth and paper are still sold in hardware and do it yourself stores, but have been largely supplanted by the increased use of machine grinding to precision size, which has minimized or eliminated the need for hand-fitting; the widespread availability of powered hand tools employing sanding and grinding accessories such as flapwheels; and a shift to other forms of abrasive, such as aluminium oxide, aluminium zirconia and silicon carbide.

Grades

Emery is rated on the average grit size, glued to the backing. Common sizes are, from coarse to fine: 40, 46, 54, 60, 70, 80, 90, 100, 120, 180, 220, 320, F, and FF. A 46 or 54 grade cloth is used on roughly filed work, while 220 to 320 grit cloth will give a good polish.[11]

Emery paper

Emery paper is a type of abrasive paper or sandpaper, that can be used to abrade (remove material from) surfaces or mechanically finish a surface. Operations include deburring, polishing, paint removal, corrosion removal, sizing, etc. This is accomplished by rubbing the abrasive-coated paper, with some pressure, against the object being processed. Abrasion may be performed by hand, electrically powered, or air powered equipment.

By the successive use of progressively finer mesh emery paper, near-mirror finishes can be obtained. Water or oil is often used as a lubricant and to float the abrasive debris and worn abrasive away from the work, preventing the build-up of debris in the emery paper. The paper will lose effectiveness if too much debris builds up, a condition known as "clogging", or "loading".

Originally, emery paper was made from milled emery rock, bonded or sized to paper often with an animal glue for water resistance.[12] Today, synthetic adhesives are used in place of natural glues and silicon carbide (SiC) is often substituted for emery, silicon carbide being slightly harder, and more durable with less tendency to fracture than corundum. The use of natural emery papers is rare today generally being replaced with silicon carbide or pure aluminium oxide papers.

Emery cloth has the abrasives bonded to a fabric instead of a paper. The cloth is more tear resistant, flexible, and costly. Emery boards have applications similar to emery paper or cloth. It also has a use in modelling. For 00 scale modelling, the fine grades of emery paper can have the appearance of a tarmac surface.

Wet & Dry

Abrasive papers and cloths with a waterproof backing allow the use of a lubricant, typically water, which can both decapitate rough surfaces when used dry and produce a semi-polished satin type finish when wet. Super-fine grades can produce a "key" adhesion surface appropriate for spray painting in critical decorative applications such as automotive bodywork repair[13][14]

Crocus

Crocus cloth is an abrasive sheet similar to sand paper or emery cloth but covered with a layer of very fine loose iron oxide particles rather than with bound grains of abrasive. It is intended for final metal and gemstone finishing and is available in various grades (particle sizes). Federal Specification P-C-458 described this material in detail, although the specification was cancelled in 1989.[15]

See also

References

  1. Casey, Don (May 3, 2016). "Know How: Sandpapers and Sanding". Sail Magazine. Retrieved 1 February 2019.
  2. Parker, Jerry (April 1962), "How to choose the right coated abrasive", Popular Science, 180 (4): 159, ISSN 0161-7370.
  3. Thomson, Keith Stewart (1992). Living Fossil: The Story of the Coelacanth. W. W. Norton & Company Limited. ISBN 978-0-393-30868-6. Archived from the original on 2014-06-27.
  4. Stalker & Parker (1971) [1688]. A Treatise of Japaning and Varnishing. Tiranti.
  5. Jeffrey, Kirk (1989). "The Major Manufacturers: From Food and Forest Products to High Technology". In Clark, Clifford Edward (ed.). Minnesota in a Century of Change: The State And Its People Since 1900. Minnesota Historical Society Press. p. 234. ISBN 978-0-87351-238-1. Archived from the original on 2014-06-27.
  6. Hill, Ray (July 1977), "PS guide to sandpaper and other coated abrasives", Popular Science, 211 (1): 106, ISSN 0161-7370.
  7. "What is the Difference Between Open and Closed Coat Abrasives?". Red Label Abrasives. Retrieved 2020-07-07.
  8. Stack, Jim (2006). Box by box. Cincinnati, Ohio: Popular Woodworking Books. ISBN 1558709436.
  9. "Sandpaper Grit". Empire Abrasives. Retrieved 13 April 2020.
  10. Dwivedi, Kamal (17 June 2021). "What is Difference Between Emery Paper and Sandpaper?". Mechical. (blog). Retrieved 2023-03-10.
  11. Oberg, Erik; Jones, Franklin D.; Horton, Holbrook L.; Ryffel, Henry H. (2000). Machinery's Handbook (26th ed.). New York: Industrial Press Inc. p. 1440. ISBN 0-8311-2635-3.
  12. Parker, John W.; Strand, West (1835). Minerals and Metals; Their Natural History and Uses in the Arts. Society for Promoting Christian Knowledge. p. 208.
  13. 3M™ Wetordry™ Sandpaper
  14. "Abrasive Wet and Dry Paper". The Polishing Shop. Retrieved 2023-03-10.
  15. "P-C-458 C Cloth Abrasive Crocus".

Further reading

  • Dresdner, Michael (1992). The Woodfinishing Book. Taunton Press. ISBN 1-56158-037-6
  • Flexner, Bob (2005). Understanding Wood Finishing — How to Select and Apply the Right Finish. Fox Chapel Publishing. ISBN Hardcover:978-1-56523-548-9. ISBN Paperback:978-1-56523-566-3
This article is issued from Wikipedia. The text is licensed under Creative Commons - Attribution - Sharealike. Additional terms may apply for the media files.